Method of forming bumps

ABSTRACT

In the conventional bump forming method that can be applied to a semiconductor device in which a large number of bumps are required to be formed, there are various limitations on the material of which the bumps are made, due to enough cubic volume of bumps and to small scattering of the bump height. According to the invention, solder balls and a tool having a large number of through-holes are used, and under the condition that the through-holes of the tool are aligned with the pads of the semiconductor device, the solder balls are charged into the through-holes, pressed to be fixed on the pads, and then reflowed to form bumps.

[0001] This application is a Continuation application of Ser. No. 09/689,804, filed Oct. 13, 2000, the contents of which are incorporated herein by reference in their entirety, which is a Continuation-in-Part application of Ser. No. 09/315,818, filed May 21, 1999, the contents of which are incorporated herein by reference in their entirety.

BACKGROUND OF THE INVENTION

[0002] The present invention relates to a method of forming bumps as electrical, mechanical and thermal connections or contacts on a semiconductor device.

[0003] There are many examples as to the method of forming bumps on a semiconductor device. For example, metal is deposited by plating to form bumps on the pads of a semiconductor device (plating method); a solder paste is printed on the pads of a semiconductor device, heated so that solder particles within the paste are melted, and thereafter solidified to form bumps on the pads (printing method); and one end of gold wire is bonded to a pad, and then the wire is cut so that the bonded part of wire is left as a bump (wire bonding method). In addition, as disclosed in U.S. Pat. No. 5,284,287, solder balls are sucked in the cavities of a pick-up tool by vacuum, placed on the pads of a semiconductor device and heated to melt, and solidified to form bumps (conventional type solder ball method).

[0004] These conventional methods, however, have the following drawbacks. In general, the larger the cubic volume of the bumps, the longer the life of the connection between the semiconductor device and an electronic circuit board through the bumps can be extended. In the plating method and printing method, however, it is difficult in principle to form bumps of enough cubic volume. Moreover, since the heights of the bumps scatter, all the bumps cannot be properly connected between the semiconductor device and, the electronic circuit board. In the wire bonding method, the material of the wire is limited to only a particular one such as gold. Also, since bumps are produced one by one, it takes a very long time to produce many pads as for a semiconductor device having tens of thousands of pads.

[0005] In the conventional type solder ball method, the scattering of the bump height is small, and bumps of enough volume can be produced, but the pick-up tool for use in sucking balls by vacuum to hold is complex in structure and requires a delicate perforating technique for very fine holes or cavities when it is produced. Since this tool becomes expensive in proportion to the number of holes required, the cost of forming bumps increases when the tool is used for a semiconductor device that needs a large number of bumps.

SUMMARY OF THE INVENTION

[0006] It is an object of the invention to provide a method of forming bumps of enough cubic volume which have small scattering of bump height and no limitation to material to be selected, and which method can be used for the bumps of a semiconductor device that needs a large number of bumps, or is able to produce bumps fast and at low cost, thus providing low-cost semiconductor devices to the market.

[0007] In order to achieve the above object, the present invention has executed the following means. First, conductive spheres such as solder balls are fundamentally used in order to provide bumps of enough cubic volume with small scattering of bump height and with no limitation to material to be selected. In addition, to actualize the high-speed, low-cost production of bumps that can be applied to the production of bumps in a semiconductor device that needs a large number of bumps, low-cost tools such as a printing metal stencil and brush that are moved in parallel are used to place a large number of solder balls on a semiconductor device at a time, which are then pushed against the pads of the semiconductor device by a pressing tool so that the bumps to be formed can be prevented from being defective, and thereafter the solder balls are heated to form bumps. Moreover, it is checked if the produced bumps are excessive or insufficient, and if necessary, re-trying operation is performed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0008]FIG. 1 is part of a flow diagram of bump formation according to the invention.

[0009]FIG. 2 is another part of a flow diagram of bump formation according to the invention.

[0010]FIG. 3 is the last part of a flow diagram of bump formation according to the invention.

[0011]FIG. 4 is a diagram of an example of a semiconductor device and a magnified part thereof.

[0012]FIG. 5 is a diagram of a tool for use in this invention.

[0013]FIGS. 6A and 6B are diagrams of the semiconductor device with flux provided.

[0014]FIG. 7 is a diagram of the tool and the semiconductor device aligned with each other, and which have a gap set between the stencil of the tool and the semiconductor device by a rectangular spacer.

[0015]FIG. 8 is a diagram of the tool and the semiconductor device aligned with each other, and which have a gap set between the stencil of the tool and the semiconductor device by a wire-shaped spacer.

[0016]FIG. 9 is a diagram of the tool and the semiconductor device aligned with each other, and which have a gap set between the stencil of the tool and the semiconductor device by a projection provided on the stencil surface.

[0017]FIG. 10 is a diagram showing an example in which a squeegee is used for a charging process.

[0018]FIG. 11 is a diagram showing another example in which air flow is used for the charging process.

[0019]FIG. 12 is a diagram showing still another example in which vibration is used for the charging process.

[0020]FIG. 13 is a diagram showing a still further example in which the tool and the semiconductor device are tilted for the charging process.

[0021]FIG. 14 is a diagram showing an example in which a pressing tool with projections is used when pressing.

[0022]FIG. 15 is a diagram showing another example in which a pressing tool with recesses is used when pressing.

[0023]FIG. 16 is a diagram showing still another example in which a pressing tool with an elastic member provided on the pressing surface is used when pressing.

[0024]FIG. 17 is a cross-sectional diagram of the through-holes of the tool with their diameter changed in the direction of their center axis.

[0025]FIG. 18 is a diagram explaining in detail the embodiment that a squeegee is applied in a charging process.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0026] An embodiment of the invention will be described with reference to FIGS. 1 to 16. In those figures, like elements are identified by the same reference numerals, and will not be repeatedly described. FIGS. 1, 2 and 3 show a fundamental flow of the bump formation according to the invention. The bump formation flow according to the invention basically includes an alignment process, a ball charging process and a heating process as illustrated in FIGS. 1, 2 and 3. These processes will hereinafter be described in order, with reference to other figures, if necessary. Referring to FIGS. 1, 2 and 3, there are shown a semiconductor device 1 on which bumps are to be formed, a tool 2, conductive spheres 3, completed bumps 4, through-holes 6 of the tool 2 that will be described later, a brush 7, and a pressing tool 9. In addition, there are shown a stencil 2 a of the tool 2, and a frame 2 b of the tool 2. Although the semiconductor device 1 on which bumps can be formed according to the invention may be of different types such as a wafer not protected, a wafer protected with resin, a cut-away part of the wafer and a packaged cut-away part of the wafer, a wafer-shaped semiconductor device is used as an example of the semiconductor device 1. This is because the effect of the invention is generally great on forming bumps of a wafer-type semiconductor device that needs a large number of bumps. FIG. 4 shows the semiconductor device 1 on which bumps are formed according to the embodiment of the invention, and a magnified part of the device. The semiconductor device 1 has a large number of pads 5 on which bumps are to be formed, for example, at most tens of thousands of pads 5. The tool 2 is formed by the frame 2 b and the stencil 2 a as illustrated by the cross-sectional view of FIG. 5. The stencil 2 a has through-holes 6 formed to oppose to the pads 5 of the semiconductor device 1.

[0027] This stencil 2 a can be made of a material of metal or resin. The diameters of the through-holes 6 are in the range from that of the electrically conductive spheres 3 to less than twice that of the spheres 3 that are used in the charging process. The through-holes 6 of this tool 2 can be formed by machining using a drill or by a chemical process such as etching or electroforming. If an appropriate one of those processes is selected according to the number of through-holes 6, the through-holes can be formed in the tool 2 at a relatively low cost.

[0028] The bump formation flow is as follows. First, an adhesive supply process is executed to supply an adhesive on the pads 5 of the semiconductor device 1. This adhesive may be flux, solder paste or conductive adhesive. The adhesive such as flux is supplied by printing with a stencil or by spin coating using centrifugal force. FIGS. 6A and 6B are cross-sectional diagrams of part of the semiconductor device 1 with an adhesive 10 provided on the pads 5 of the semiconductor device 1. FIG. 6A shows the adhesive 10 coated over the entire surface of the semiconductor device 1 including the pads 5, and FIG. 6B shows the adhesive 10 selectively coated only on the pads of the device 1.

[0029] Next, the alignment process is executed to align the pads 5 of the semiconductor device 1 with the through-holes 6 of the tool 2. The alignment is performed manually by usual recognition as in the stencil printer or automatically by using an automatic stage and image processing that pays attention to the features of a video image picked up by a CCD camera. FIG. 7 is a magnified view of the completed alignment between the device 1 and the tool 2. In FIG. 7, there is shown a rectangular spacer 8 a that is set between the device 1 and the tool 2 in order to fix the gap therebetween. FIG. 8 shows an example of using a wire-shaped spacer 8 b. FIG. 9 shows an example of using a spacer 8 c that is integrally formed with the tool 2. These spacers can prevent the through-holes 6 from being contaminated with the adhesive 10 such as flux that is coated on the pads 5 of the semiconductor device 1. In other words, if the height of the spacer is selected to be larger than that of the supplied adhesive 10 such as flux, there is no risk that the tool 2 is made in contact with the adhesive such as flux.

[0030] In the ball charging process, the conductive spheres 3 of which the number is larger than that of the bumps being formed are supplied on the tool 2. The supplied conductive spheres 3 are dropped down into the through-holes 6 of the tool 2 by the translational motion of the brush 7 shown in FIG. 2, or the through-holes 6 are charged with the conductive spheres 3. In addition, the excessive conductive spheres 3 on the tool 2 are removed from the regions in which the through-holes 6 occupy on the tool 2 by the translation of the brush 7. In order that the number of spheres 3 charged into one through-hole 6 of the tool 2 is limited to one, the dimension h shown in FIG. 7 is required to be less than 1.5 times as large as the diameter of the conductive sphere 3. The charging of conductive spheres 3 into the though-holes 6 of the tool 2 can be performed not only by using the brush 7, but also by using the translation of a squeegee 11 (e.g., in the form of a spatula) shown in FIG. 10, using an air flow 13 from an air nozzle 12 shown in FIG. 11, the vibration shown in FIG. 12 or the tilting of the tool 2 and device 1 shown in FIG. 13. Also, the excessive conductive spheres 3 can be removed from around the through-holes 6 by those means. Thereafter, if necessary, tests are made to examine if the through-holes 6 have been completely charged with the spheres, and if the excessive spheres 3 have been completely removed from around the through-holes 6, thus making sure of the processes. The tests can be performed by the usual recognition of the operator or by the automatic recognition using the combination of the electric CCD and image processor. If the charging operation and the excessive sphere removal are found not to be complete, the charging process is repeated, the spheres 3 are added, or the excessive conductive spheres 3 are directly removed by workers, thus solving those problems.

[0031]FIG. 18 shows in detail a ball charging process using a squeegee. In FIG. 18, the pads 5 and the adhesive 10 are depicted thicker than the practical proportion for identifying distinctively in FIG. 18. Here, a spacer 8 c is formed with a tool in one body, and a height of a surface of the tool 2 (that is, the upper surface 2 e of the tool) is kept at least 0.8 times the diameter of the conductive sphere, and, e.g., smaller than the diameter of the conductive sphere, for example, 0.9 times of the diameter of the conductive sphere, from a surface of the semiconductor device 1. A gap between the tool 2 and the semiconductor device 1 (that is, a gap between the semiconductor device and a bottom surface 2 f of the tool 2) is kept at most 0.5 times the diameter of the conductive sphere, e.g., 0.4 times of the diameter of the conductive sphere 3. For such a configuration, the succeeding pressing operation becomes easy, and it eliminates a problem that the bottom (under) surface 2 f of the tool becomes dirty by flux. Further, since the diameter of the through-hole 6 of the tool 2 is 1.2 times of the diameter of the conductive sphere 3, the conductive sphere is filled into the through-hole 6 easily, and the conductive spheres equal to or more than two cannot be filed into the through-hole 6 simultaneously. In addition, the height of the under surface 11 c of the squeegee 11 is kept at most 0.5 times the diameter of the conductive sphere 3, e.g., 0.3 times of the diameter of the conductive sphere 3, from the upper surface 2 e of the tool 2 by the spacer 11 a disposed remotely in the direction of the sheet of FIG. 18, so that the surface of the squeegee 11 facing with the conductive sphere 3 is kept almost perpendicular to the surface of the semiconductor device 1. Therefore, the conductive sphere 3 a already filled in exists in the surface of the semiconductor device 1 stably without contacting with the squeegee 11. The conductive sphere 3 b is filled in before the squeegee 11 advances in the direction of arrow 11 e; and, before the squeegee 11 advances, the excessive conductive sphere 3 c is disposed on the gap between the tool 2 and the already positioned conductive sphere 3 b. The squeegee 11, as it moves in the direction of arrow lie, presses against the excessive conductive sphere 3 c; the direction of the pressing (compression) force is along a horizontal plane (e.g., parallel to surface 2 e of tool 2), so that the excessive conductive sphere 3 c can be eliminated effectively. Here, since the contact angle of the excessive conductive sphere 3 c and the conductive sphere 3 b already filled in through-hole 6 is a almost horizontal plane, the force necessary for the squeegee 11 to eliminate is small enough. Namely, since both the excessive conductive sphere 3 c and the conductive sphere 3 b already filled in through-hole 6 are not subjected to the excessive stress, the deformations of the pressing trace, the abrasion and so on are not sustained. Further, the excessive conductive sphere 3 c is filled successively into the through-holes 6 not filled yet with the advance of the squeegee 11, similarly to the conductive spheres 3 d disposed on the tool. Eventually, the conductive spheres 3 which are not used are accumulated at the edge of the tool 2, so that the conductive spheres are retrieved for the next usage. Here, if a pair of squeegees 11 is provided, the conductive spheres not used can be moved adversely by the other squeegee not used, so that a plurality of filling processes can be performed successively. Further, there exist the advantages of reducing the dissipation of the conductive spheres during the charging process and of retrieving the conductive spheres not used exactly.

[0032] After the completion of the charging of conductive spheres into the through-holes 6 and the removal of excessive conductive spheres 3 from around the through-holes 6, the pressing tool 9 is moved up and down to press the conductive spheres 3 in the through-holes 6 against the semiconductor device 1. After the pressure, the tool 2 is lifted away from the semiconductor device 1. In this case, since the conductive spheres 3 stuffed in the through-holes 6 are pressed down, the spheres 3 are closely attached to the pads 5 and thus securely fixed on the pads 5 by the adhesion of the adhesive 10. Therefore, when the tool 2 is pulled up from the semiconductor device 1, the conductive spheres 3 are left on the semiconductor device 1, and they are never moved up with the tool 2 due to the positional deviation or sticking to the inner walls of the through-holes 6. In some case, after the tool 2 is pulled up, the conductive spheres 3 on the pads 5 may be again pressed by the pressing tool 9 in order to increase the effectiveness. By the second pressing, the displacement of spheres 3 that may be caused by the subsequent conveyance and heating process can be suppressed to the minimum. The pressing tool 9 may have not only simply a flat plate for pressing, but also projections shown in FIG. 14, recesses shown in FIG. 15 or an elastic body shown in FIG. 16. The pressing tool 9 having projections for use in pressing before the removal of the tool 2 has an effect of enabling the thickness of the stencil of the tool 2 to be made larger than the diameter of the conductive sphere as shown in FIG. 14. Thus, since the rigidity-of the tool 2 can be enhanced, the life of the tool can be extended. By using the pressing tool 9 having recesses on the pressing side, it is possible to precisely position the conductive spheres 3 on the pads 5 of the semiconductor device 1. In addition, by using the pressing tool 9 having an elastic body on the pressing side, it is possible to press all the conductive spheres irrespective of the dimensional allowances. If an appropriate method of forming the through-holes 6, of which the diameter was described previously, is developed to be able to change the diameter of the through-holes 6 in the thickness direction of the stencil 2 a of tool 2 as shown in FIG. 17, the conductive spheres 3 can be easily stuffed into the through-holes 6 and placed on the pads 5 of the device 1 with high precision. In this case, it is desired that on the side where the conductive spheres 3 are supplied, the diameter of the through-hole 6 is equal to or larger than the diameter of the conductive sphere 3 and less than twice of the diameter of the conductive sphere 3 (e.g., less than 1.3 times the diameter of the conductive sphere 3), and on the side of the pad 5, the diameter of the conductive sphere is near to the diameter of the conductive sphere 3 and larger than the diameter of the conductive sphere 3.

[0033] In the following heating step, the semiconductor device 1 with the conductive spheres 3 mounted on the pads is placed in a heating furnace such as a commercially available reflow furnace. Thus, the conductive spheres 3 can be changed into the bumps 4 connected to the pads of the device 1. Thereafter, if necessary, the semiconductor device 1 is rinsed, and cut into necessary sizes, thus the device 1 with the bumps 4 being completed.

[0034] In this embodiment, tens of thousands of bumps can be formed at a time on the pads 5 of the semiconductor device 1, thus the mass productivity of bumps being remarkably improved.

[0035] According to the invention, a large number of bumps can be formed at a time on the pads of the semiconductor device. In addition, the tool and so on for the production of bumps can be used at low cost, and the device structure can be made simple. Moreover, since conductive spheres such as solder balls can be used as the bump material, bumps of different constituents can be formed. The bridging and ball vanishing problems sometimes caused when conductive spheres such as solder balls are used can be solved by providing the process for pressing the conductive spheres against the pads.

[0036] Many different embodiments of the present invention may be constructed without departing from the spirit and scope of the invention. It should be understood that the present invention is not limited to the specific embodiments described in this specification. To the contrary, the present invention is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the claims. 

What is claimed is:
 1. A method of forming bumps in which conductive spheres are used to form bumps on a semiconductor device, comprising the steps of: aligning a tool having through-holes with said semiconductor device so that said through-holes can be opposed to the places where said bumps are to be formed; supplying said conductive spheres on said tool, charging said conductive spheres into said through-holes of said tool and removing said tool from said semiconductor device as a ball charging process; and heating said conductive spheres and said semiconductor device, wherein diameters of said through-holes of said tool on a surface that said conductive spheres are filled into are equal to or larger than diameters of said conductive spheres and smaller than 1.3 times of said diameters of said conductive spheres, and diameters of said through-holes of said tool on a surface facing with said semiconductor device is equal to or larger than diameters of said conductive spheres.
 2. A method of forming bumps in which conductive spheres are used to form bumps on a semiconductor device, comprising the steps of: aligning a tool having through-holes with said semiconductor device so that said through-holes can be opposed to the places where said bumps are to be formed; supplying said conductive spheres on said tool, charging said conductive spheres into said through-holes of said tool and removing said tool from said semiconductor device as a ball charging process; and heating said conductive spheres and said semiconductor device, wherein a height of said through-holes of said tool from a surface of said semiconductor device is at least 0.8 times a diameter of said conductive spheres and smaller than said diameter of said conductive spheres, and a distance between a bottom surface of said through-holes and said surface of said semiconductor device is equal to or smaller than 0.5 times the diameter of said conductive spheres.
 3. A method of forming bumps in which conductive spheres are used to form bumps on a semiconductor device, comprising the steps of: aligning a tool having through-holes with said semiconductor device so that said through-holes can be opposed to the places where said bumps are to be formed; supplying said conductive spheres on said tool, charging said conductive spheres into said through-holes of said tool and removing said tool from said semiconductor device as a ball charging process, the charging of the conductive spheres into said through-holes including moving a squeegee along the tool; and heating said conductive spheres and said semiconductor device, wherein a squeegee gap is set between an upper surface of the tool and the squeegee, such that a bottom surface of the squeegee is at a height above the tool wherein the squeegee does not contact with said conductive spheres filled in said through-holes, and said squeegee gap is equal to or smaller than 0.5 times of a diameter of said conductive spheres disposed on said tool in translation motion of the squeegee. 